| 特性级别 | 标准级||| |
| 牌号 | LUX2614 resin |
| 加工级别 | 注堕级|||热熔级||| |
| 品名 | * LEXAN LUX2614 resin |
| 厂家(产地) | 沙伯基础（原GE） |
| 用途级别 | 通用级||| |
* LEXAN LUX2614 resin
生产企业：沙伯基础（原GE）
规格用途
| 规格级别 | 阻燃 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D792 | 1.20 | g/cm3 | |
| ASTM D792 | 1.19 | g/cm3 | |||
特定体积 | ASTM D792 | 0.830 | cm3/g | ||
| 熔流率 | (300°C/1.2 kg) | ASTM D1238 | 7 | g/10 min | |
| 收缩率 - 流动 | (3.20 mm) | Internal Method | 0.50到 0.70 | % | |
吸水率 | 24 hr | ASTM D570 | 0.15 | % | |
平衡, 23°C | ASTM D570 | 0.35 | % | ||
平衡, 100°C | ASTM D570 | 0.58 | % | ||
室外适用性 | UL 746C | f2 | |||
| 硬度 | 洛氏硬度 | M 计秤 | ASTM D785 | 70 | |
R 计秤 | ASTM D785 | 118 | |||
| 机械性能 | 抗张强度 | 屈服,Type I, 5 mm/min | ASTM D638 | 62.1 | MPa |
| 断裂,Type I, 5 mm/min | ASTM D638 | 65.5 | MPa | ||
伸长率 | 屈服,Type I, 5 mm/min | ASTM D638 | 7.0 | % | |
| 断裂,Type I, 5 mm/min | ASTM D638 | 110 | % | ||
弯曲模量 | 50.0 mm 跨距,1.3 mm/min | ASTM D790 | 2340 | MPa | |
弯曲强度 | 屈服, 50.0 mm 跨距,1.3 mm/min | ASTM D790 | 93.1 | MPa | |
| 抗泰伯磨耗 | (1000 Cycles, 1000 g, CS-17 转轮) | ASTM D1044 | 10.0 | mg | |
| 冲击性能 | 悬壁梁缺口冲击强度 | 23°C | ASTM D256 | 750 | J/m |
无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 3200 | J/m | |
| 落锤冲击 | (23°C) | ASTM D3029 | 169 | J | |
| 拉伸冲击强度 | Type S | ASTM D1822 | 546 | kJ/m2 | |
| 热性能 | 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 138 | °C |
1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 132 | °C | ||
维卡软化温度 | 标准 B (120°C/h), 压 力2 (50N) | ASTM D1525 | 154 | °C | |
| Ball Pressure Test | (125°C) | Pass | IEC 60695-10-2 | ||
线形膨胀系数 | 流动: -40 到 95°C | ASTM E831 | 0.000068 | cm/cm/°C | |
比热 | ASTM C351 | 1260 | J/kg/°C | ||
导热系数 | ASTM C177 | 0.29 | W/m/K | ||
RTI Elec | UL 746 | 80.0 | °C | ||
RTI Imp | UL 746 | 80.0 | °C | ||
RTI Str | UL 746 | 80.0 | °C | ||
| 电气性能 | 体积电阻率 | ASTM D257 | > 1.0E+17 | ohm·cm | |
介电强度 | (3.20 mm, in Air) | ASTM D149 | 15 | kV/mm | |
介电常数 | 50 Hz | ASTM D150 | 3.17 | ||
60 Hz | ASTM D150 | 3.17 | |||
1 MHz | ASTM D150 | 2.96 | |||
耗散因数 | 50 Hz | ASTM D150 | 0.00090 | ||
60 Hz | ASTM D150 | 0.00090 | |||
1 MHz | ASTM D150 | 0.010 | |||
相比耐漏电起痕指数(CTI) | UL 746A | 3 | PLC code | ||
高电弧燃烧指数(HAI) | UL 746A | 1 | PLC code | ||
热丝引燃 (HWI) | UL 746A | 3 | PLC code | ||
| 可燃性 | UL 阻燃等级 | 0.75 - 1.65 | V-2 | UL 94 | |
灼热丝易燃指数 | 0.750 mm | IEC 60695-2-12 | 750 | °C | |
| 1.50mm | IEC 60695-2-12 | 850 | °C | ||
热灯丝点火温度 | 0.750 mm by VDE | IEC 60695-2-13 | 875 | °C | |
1.50 mm | IEC 60695-2-13 | 850 | °C | ||
| 注射 | 干燥温度 | 120 | °C | ||
干燥时间 | 3到4 | hr | |||
干燥时间，* | 48 | hr | |||
建议的*水分含量 | 0.02 | % | |||
建议注入量 | 40到60 | % | |||
螺筒后部温度 | 290 到 310 | °C | |||
螺筒中部温度 | 300 到 320 | °C | |||
螺筒前部温度 | 310 到 330 | °C | |||
射嘴温度 | 305 到 325 | °C | |||
加工（熔体）温度 | 310 到 330 | °C | |||
模具温度 | 80到115 | °C | |||
背压 | 0.3到0.7 | MPa | |||
螺杆转速 | 40 到 70 | rpm | |||
排气孔深度 | 0.025 到 0.076 | mm | |||
* LEXAN LUX2614 resin