| 品牌 | 基础创新塑料(南沙) |
| 货号 | 141R-701 |
| 用途 | 塑胶产品 |
| 牌号 | 141R-701 |
| 型号 | 141R-701 |
| 品名 | 塑料原料 |
| 外形尺寸 | 25KG一包 |
| 生产企业 | 基础创新塑料(南沙) |
| 是否进口 | 是 |
* 141R-701 * 基础创新塑料(南沙) 141R-701
规格用途
| 规格级别 | 其它 其它 吹塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1.5 | g/10min |
| 190℃/2.16kg | ISO 1133 | 1.5 | g/10min | ||
| 单体含量 | Internal Method | 9.7 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.938 | g/cm3 | |
| ISO 1183 | 0.938 | g/cm3 | |||
| 机械性能 | 拉伸屈服强度 | Compression Molded | ASTM D-638 | 8.39 | MPa |
| Compression Molded | ISO 527-2/508 | 8.39 | MPa | ||
| 拉伸断裂强度 | Compression Molded | ASTM D-638 | 22.5 | MPa | |
| Compression Molded | ISO 527-2/508 | 22.5 | MPa | ||
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 640 | % | |
| Compression Molded | ISO 527-2/508 | 640 | % | ||
| 薄膜厚度-Tested | 50.8 | um | |||
| 拉伸屈服强度(MD) | 50.8um | ASTM D-882 | 11.8 | MPa | |
| 拉伸屈服强度(TD) | 50.8um | ASTM D-882 | 10.9 | MPa | |
| 50.8um | ISO 527-3 | 10.9 | MPa | ||
| 拉伸屈服强度(MD) | 50.8um | ISO 527-3 | 11.8 | MPa | |
| 拉伸断裂强度(TD) | 50.8um | ASTM D-882 | 38.1 | MPa | |
| 拉伸断裂强度(MD) | 50.8um | ASTM D-882 | 37.9 | MPa | |
| 50.8um | ISO 527-3 | 37.9 | MPa | ||
| 拉伸断裂强度(TD) | 50.8um | ISO 527-3 | 38.1 | MPa | |
| 拉伸断裂伸长率(TD) | 50.8um | ASTM D-882 | 470 | % | |
| 拉伸断裂伸长率(MD) | 50.8um | ASTM D-882 | 400 | % | |
| 50.8um | ISO 527-3 | 400 | % | ||
| 拉伸断裂伸长率(TD) | 50.8um | ISO 527-3 | 470 | % | |
| 落锤冲击 | 50.8um | ASTM D-1709B | 580 | g | |
| 50.8um | ISO 7765-1/B | 580 | g | ||
| 埃尔曼多夫撕裂强度(TD) | 50.8um | ASTM D-1922 | 510 | g | |
| 埃尔曼多夫撕裂强度(MD) | 50.8um | ASTM D-1922 | 380 | g | |
| 50.8um | ISO 6383-2 | 1700 | N | ||
| 埃尔曼多夫撕裂强度(TD) | 50.8um | ISO 6383-2 | 2300 | N | |
| 热性能 | 维卡软化点 | ASTM D-1525 | 81.1 | ℃ | |
| ISO 306 | 81.1 | ℃ | |||
| 熔融温度 | Internal Method | 97.8 | ℃ | ||
| 光学性能 | 光泽度 | 45°，50.8um | ASTM D-2457 | 65 | |
| 雾度 | 50.8um | ISO 14782 | 5.8 | % | |
| 50.8um | ASTM D-1003 | 5.8 | % | ||
* 141R-701 * 基础创新塑料(南沙) 141R-701