| 品牌 | 基础创新塑料(南沙) |
| 货号 | EXL9330-GY2E408 |
| 用途 | 塑胶产品 |
| 牌号 | EXL9330-GY2E408 |
| 型号 | EXL9330-GY2E408 |
| 品名 | 塑料原料 |
| 外形尺寸 | 25KG一包 |
| 生产企业 | 基础创新塑料(南沙) |
| 是否进口 | 是 |
* EXL9330-GY2E408 * 基础创新塑料(南沙) EXL9330-GY2E408
规格用途
| 规格级别 | 其它 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 特性：良好的热稳定性 | ||
技术参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 | % |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- | % | ||
| 饱和(23℃) | ASTM D-570 | DAM｜7.0 | % | ||
| 饱和(23℃) | ASTM D-570 | 50%RH｜- | % | ||
| 物理性能 | 比重 | ASTM D-792 | DAM｜1.09 | ||
| ASTM D-792 | 50%RH｜1.09 | ||||
| 机械性能 | 断裂伸长率 | 23℃ | ASTM D-638 | DAM｜80 | % |
| 23℃ | ASTM D-638 | 50%RH｜270 | % | ||
| 揉曲模量 | 23℃ | ASTM D-790 | DAM｜1965 | MPa | |
| 23℃ | ASTM D-790 | 50%RH｜1103 | MPa | ||
| 洛氏硬度M | ASTM D-785 | DAM｜M71 | |||
| ASTM D-785 | 50%RH｜M50 | ||||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | DAM｜230 | J/m | |
| 23℃ | ASTM D-256 | 50%RH｜240 | J/m | ||
| 硬度计硬度 | ASTM D-676 | DAM｜83 | |||
| ASTM D-676 | 50%RH｜76 | ||||
| 洛氏硬度R | ASTM D-785 | DAM｜R115 | |||
| ASTM D-785 | 50%RH｜R102 | ||||
| 屈服伸长率 | ASTM D-638 | DAM｜5 | % | ||
| ASTM D-638 | 50%RH｜15 | % | |||
| 屈服强度 | 23℃ | DAM｜60.7 | MPa | ||
| 23℃ | 50%RH｜51.7 | MPa | |||
| 拉伸冲击强度 | 长试样23℃ | ASTM D-1822 | DAM｜550 | KJ/m2 | |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1680 | KJ/m2 | ||
| 短试样23℃ | ASTM D-1822 | DAM｜189 | KJ/m2 | ||
| 短试样23℃ | ASTM D-1822 | 50%RH｜265 | KJ/m2 | ||
| 拉伸强度 | 23℃ | ASTM D-638 | DAM｜62.1 | MPa | |
| 23℃ | ASTM D-638 | 50%RH｜51.7 | MPa | ||
| 电气性能 | 体积电阻率 | ASTM D-257 | DAM｜1013 | Ω.m | |
| ASTM D-257 | 50%RH｜1013 | Ω.m | |||
| 介电常数 | 103Hz(cps) | ASTM D-150 | DAM｜3.1 | ||
| 100Hz(cps) | ASTM D-150 | 50%RH｜4.8 | |||
| 耗散因数 | 100Hz(cps) | ASTM D-150 | DAM｜0.02 | ||
| 100Hz(cps) | ASTM D-150 | 50%RH｜0.1 | |||
| 103Hz(cps) | ASTM D-150 | DAM｜0.02 | |||
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.11 | |||
| 106Hz(cps) | ASTM D-150 | DAM｜0.02 | |||
| 106Hz(cps) | ASTM D-150 | 50%RH｜0.10 | |||
| 介电常数 | 106Hz(cps) | ASTM D-150 | DAM｜2.9 | ||
| 106Hz(cps) | ASTM D-150 | 50%RH｜3.3 | |||
| 热性能 | 热畸变温度 | (0.5)×106Pa | ASTM D-648 | DAM｜230 | ℃ |
| (0.5)×106Pa | ASTM D-648 | 50%RH｜- | ℃ | ||
| UL可燃性导级 | UL 94 | DAM｜94 | |||
| UL 94 | 50%RH｜HB | ||||
| 熔点结晶 | ASTM D-2177 | DAM｜270 | ℃ | ||
| ASTM D-2177 | 50%RH｜- | ℃ | |||
| 线性热膨胀系数 | ASTM D-696 | DAM｜7×10-5 | m/m/℃ | ||
| ASTM D-696 | 50%RH｜- | m/m/℃ | |||
| 荷重形变 | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 | % | |
| 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- | % | ||
| 熔点 | Fisher Johns法 | ASTM D-789 | DAM｜255 | ℃ | |
| Fisher Johns法 | ASTM D-789 | 50%RH｜255 | ℃ | ||
| 热畸变温度 | 18×106Pa | ASTM D-648 | DAM｜75 | ℃ | |
| 18×106Pa | ASTM D-648 | 50%RH｜- | ℃ | ||
| 脆化温度 | ASTM D-746 | DAM｜-104 | ℃ | ||
| ASTM D-746 | 50%RH｜-84 | ℃ | |||
* EXL9330-GY2E408 * 基础创新塑料(南沙) EXL9330-GY2E408